Tribochemical wear of cutting-tool ceramics in sliding contact against a nickel-base alloy A Renz, I Khader, A Kailer Journal of the European Ceramic Society 36 (3), 705-717, 2016 | 50 | 2016 |
A wear model for silicon nitride in dry sliding contact against a nickel-base alloy I Khader, A Renz, A Kailer Wear 376, 352-362, 2017 | 32 | 2017 |
Hydrogen assisted rolling contact fatigue due to lubricant degradation and formation of white etching areas D Kürten, I Khader, R Raga, P Casajús, N Winzer, A Kailer, R Spallek, ... Engineering Failure Analysis 99, 330-342, 2019 | 30 | 2019 |
A study on the wear of silicon nitride in rolling–sliding contact I Khader, D Kürten, A Kailer Wear 296 (1-2), 630-637, 2012 | 29 | 2012 |
Characterization of a silicon nitride ceramic material for ceramic springs I Khader, C Koplin, C Schröder, J Stockmann, W Beckert, W Kunz, ... Journal of the European Ceramic Society 40 (10), 3541-3554, 2020 | 27 | 2020 |
Thermal and corrosion properties of silicon nitride for copper die casting components I Khader, A Renz, A Kailer, D Haas Journal of the European Ceramic Society 33 (3), 593-602, 2013 | 22 | 2013 |
Wear and corrosion of silicon nitride rolling tools in copper rolling I Khader, A Hashibon, JM Albina, A Kailer Wear 271 (9-10), 2531-2541, 2011 | 22 | 2011 |
High temperature tribological properties of silicon nitride in dry sliding contact against Inconel 718 heated by laser B Zhao, I Khader, R Raga, G Konrath, U Degenhardt, A Kailer Wear 434, 203000, 2019 | 20 | 2019 |
Modeling hydrogen diffusion in a tribological scenario: A failure analysis of a thrust bearing I Khader, D Kürten, R Raga, N Winzer, A Kailer Wear 438, 203054, 2019 | 19 | 2019 |
Damage initiation and evolution in silicon nitride under non-conforming lubricated hybrid rolling contact R Raga, I Khader, Z Chlup, A Kailer Wear 360, 147-159, 2016 | 19 | 2016 |
Tribological behavior of three silicon nitride ceramics in dry sliding contact against Inconel 718 over a wide range of velocities B Zhao, I Khader, R Raga, U Degenhardt, A Kailer Wear 448, 203206, 2020 | 16 | 2020 |
Tribochemical degradation of vacuum‐stable lubricants: A comparative study between multialkylated cyclopentane and perfluoropolyether in a vacuum ball‐on‐disc and full‐bearing … D Kürten, I Khader, A Kailer Lubrication Science, 1– 9, 2020 | 16 | 2020 |
Lifetime prediction of ceramic components–A case study on hybrid rolling contact I Khader, S Rasche, T Lube, R Raga, U Degenhardt, A Kailer Engineering Fracture Mechanics 169, 292-308, 2017 | 14 | 2017 |
Hydrogen diffusion and trapping in bodies undergoing rolling contact N Winzer, I Khader Wear 303 (1-2), 451-458, 2013 | 14 | 2013 |
Probabilistic lifetime prediction for ceramic components in rolling applications M Härtelt, H Riesch-Oppermann, I Khader, O Kraft Journal of the European Ceramic Society 32 (10), 2073-2085, 2012 | 12 | 2012 |
Damage mechanisms in silicon nitride wire-rolling tools: Lab-scale experiments and correlation with finite element modeling I Khader, A Kailer Journal of Materials Processing Technology 210 (10), 1314-1325, 2010 | 11 | 2010 |
Determining the effective hydrogen diffusion coefficient in 100Cr6 D Kürten, I Khader, A Kailer Materials and Corrosion 71 (6), 918-923, 2020 | 8 | 2020 |
Tribological characterization of an alumina-based composite in dry sliding contact against laser-heated and unheated Inconel 718 B Zhao, I Khader, H Liu, T Zhou, G Konrath, A Kailer Tribology International 155, 106773, 2021 | 7 | 2021 |
Damage progression in silicon nitride undergoing non-conforming hybrid cyclic contact R Raga, I Khader, Z Chlup, A Kailer International Journal of Fatigue 105, 97-110, 2017 | 7 | 2017 |
Damage mechanisms in silicon nitride rolling tools applied in caliber rolling copper and steel wires I Khader Shaker, 2010 | 5 | 2010 |